PA66 A3W PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 BASF GERMANY A3W

Enhanced level

US$ 4,630 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	BASF GERMANY/A3W
Volume resistivity	干/湿		10 Ω.cm
Dielectric strength	K20/P50，干/湿		120/60 KV/mm
Loss angle	1MHz，干/湿		0.025/0.2
Surface resistivity	干/湿		10 Ω
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 500
Volume resistivity		ASTM D257/IEC 60093	1E 13 Ω.cm
Dielectric constant	1MHz，干/湿		3.5/7
mechanical properties	Test Condition	Test Method	BASF GERMANY/A3W
Impact strength of cantilever beam gap	+23℃，干/湿		5.5/NB KJ/m
Charpy Notched Impact Strength	+23℃，干/湿		NB/NB KJ/m
impact strength	-20℃,干		30 J
Elongation at Break	干/湿，V=50mm/min		4.4/20 %
Tensile modulus		ASTM D638/ISO 527	3000 kg/cm²(MPa)[Lb/in²]
impact strength	+23℃，干/湿		75/>140 J
Fracture stress (V=50mm/min)	干/湿		85/50 Mpa
Tensile creep modulus	1000h,湿		700 Mpa
Tensile modulus	干/湿		3000/1000 Mpa
Ball Pressure Test	干/湿		160/100 Mpa
Impact strength of cantilever beam gap	-30℃,干		6 KJ/m
Bending modulus		ASTM D790/ISO 178	2900 kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	85屈服 kg/cm²(MPa)[Lb/in²]
Bending modulus	干/湿		3100 Mpa
Tensile yield stress (V=50mm/min)	干/湿		85/50 Mpa
other	Test Condition	Test Method	BASF GERMANY/A3W
characteristic			多种工程部件和机械零件（如优质电绝缘材料）及多种特殊应用
remarks			高机械强度、刚度和热稳定性.低温抗冲击性、滑动摩擦性
thermal performance	Test Condition	Test Method	BASF GERMANY/A3W
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.7-1 mm/mm.℃
Temperature index	在20000h/5000h，后拉伸强度下降50%时		121/147 °C
Maximum operating temperature			>200 °C
Hot deformation temperature	0.45MPa负荷，Dry		220 °C
Hot deformation temperature		1.8MPa负荷，Dry		75 °C
specific heat	Dry		1.7 J/(g.K)
Linear coefficient of thermal expansion	（23-80）℃，Dry		7-10
thermal conductivity	Dry		0.23 W/(m.K)
Melting temperature			260 ℃（℉）
Physical properties	Test Condition	Test Method	BASF GERMANY/A3W
Shrinkage rate		ASTM D955	/0.85 %
density		ASTM D792/ISO 1183	1130
Other performance	Test Condition	Test Method	BASF GERMANY/A3W
elongation	≤0.5%, +23℃，湿		700 Mpa