PA66 A3W BASF GERMANY

195

Form：Granules | Grade：Enhanced level

Properties:

Oil resistantFast forming cycleHigh mobilityheat-resisting

Typical Applications:

wheelEngine partsLaptop casebearing

Supplier(3)

Product Description

Certificates(1)

Datasheet

Alternative(1)

Product Description

Typical Applications:	wheel \| Engine parts \| Laptop case \| bearing
Properties:	Oil resistant \| Fast forming cycle \| High mobility \| heat-resisting

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
remarks			高机械强度、刚度和热稳定性.低温抗冲击性、滑动摩擦性
characteristic			多种工程部件和机械零件（如优质电绝缘材料）及多种特殊应用
Other performance	Test Condition	Test Method	Test Result	Test Unit
elongation	≤0.5%, +23℃，湿		700	Mpa
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile yield stress (V=50mm/min)	干/湿		85/50	Mpa
impact strength	-20℃,干		30	J
Elongation at Break	干/湿，V=50mm/min		4.4/20	%
Tensile creep modulus	1000h,湿		700	Mpa
Charpy Notched Impact Strength	+23℃，干/湿		6/20	KJ/m
impact strength	+23℃，干/湿		75/>140	J
Ball Pressure Test	干/湿		160/100	Mpa
Tensile modulus	干/湿		3000/1000	Mpa
Fracture stress (V=50mm/min)	干/湿		85/50	Mpa
Impact strength of cantilever beam gap	+23℃，干/湿		5.5/NB	KJ/m
Charpy Notched Impact Strength	+23℃，干/湿		NB/NB	KJ/m
Elongation at Break	干/湿，V=50mm/min		4.4/20	%
Bending modulus	干/湿		3100	Mpa
Impact strength of cantilever beam gap	-30℃,干		6	KJ/m
Tensile modulus		ASTM D638/ISO 527	3000	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	85屈服	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2900	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa负荷，Dry		75	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa负荷，Dry		220	°C
specific heat	Dry		1.7	J/(g.K)
Maximum operating temperature			>200	°C
thermal conductivity	Dry		0.23	W/(m.K)
Linear coefficient of thermal expansion	（23-80）℃，Dry		7-10
Temperature index	在20000h/5000h，后拉伸强度下降50%时		121/147	°C
Melting temperature			260	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.7-1	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1130
Shrinkage rate		ASTM D955	/0.85	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity	干/湿		10	Ω
Dielectric constant	1MHz，干/湿		3.5/7
Loss angle	1MHz，干/湿		0.025/0.2
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 475 M
Volume resistivity	干/湿		10	Ω.cm
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 500
Dielectric strength	K20/P50，干/湿		120/60	KV/mm
Volume resistivity		ASTM D257/IEC 60093	1E 13	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 A3W BASF GERMANY

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index