PA66 101L PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 DUPONT SINGAPORE 101L

Injection grade

US$ 3,720 / MT

FOB Dongguan Port

Physical properties	Test Condition	Test Method	DUPONT SINGAPORE/101L
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	8.5 %
density		ISO 1183	1.14 g/cm³
Stickiness	96% H2SO4	ISO 307	150 cm³/g
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.6 %
Shrinkage rate	Flow	ISO 294-4	1.4 %
Shrinkage rate		横向Flow	ISO 294-4	1.4 %
thermal performance	Test Condition	Test Method	DUPONT SINGAPORE/101L
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4 cm/cm/°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	190 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	70.0 °C
Melting temperature		ISO 11357-3	262 °C
Vicat softening temperature		ISO 306/B50	240 °C
Effective thermal diffusivity coefficient			5.00E-8 m²/s
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.0E-4 cm/cm/°C
Glass transition temperature		ISO 11357-2	60.0 °C
injection	Test Condition	Test Method	DUPONT SINGAPORE/101L
Melt Temperature, Optimum			290 °C
Hold Pressure Time			4.00 s/mm
Mold temperature			50 to 90 °C
Processing (melt) temperature			280 to 300 °C
Maximum Screw Tangential Speed			24 m/min
Maintain pressure			50.0 to 100 Mpa
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
drying temperature			80 °C
Mold Temperature, Optimum			70 °C
Maintain pressure	Drying Recommended		yes
flammability	Test Condition	Test Method	DUPONT SINGAPORE/101L
FMVSS combustion rate		FMVSS 302	DNI
Atomization	G-value (condensate)	ISO 6452	1.0E-4 g
Extreme Oxygen Index		ISO 4589-2	28 %
UL flame retardant rating		UL 94	V-2
Atomization	F-value (refraction)	ISO 6452	99 %
Filling analysis	Test Condition	Test Method	DUPONT SINGAPORE/101L
Odor		VDA 270	3.00
Top out temperature			190 °C
Melt density			0.970 g/cm³
Thermal Conductivity of Melt			0.16 W/m/K
Specific Heat Capacity of Melt			2790 J/kg/°C
Emission of Organic Compounds		VDA 277	5.00 µgC/g
Electrical performance	Test Condition	Test Method	DUPONT SINGAPORE/101L
Dissipation factor	100 Hz	IEC 62631-2-1	8.0E-3
Volume resistivity		IEC 62631-3-1	1.0E+12 ohms·m
Surface resistivity		IEC 62631-3-2	-- ohms
Dielectric strength		IEC 60243-1	32 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	1 MHz	IEC 62631-2-1	0.018
Relative permittivity	100 Hz	IEC 62631-2-1	3.80
Relative permittivity		1 MHz	IEC 62631-2-1	3.50
film	Test Condition	Test Method	DUPONT SINGAPORE/101L
elongation	Yield， MD	ISO 527-3	4.5 %
mechanical properties	Test Condition	Test Method	DUPONT SINGAPORE/101L
Tensile modulus		ISO 527-2	3100 Mpa
Nominal tensile fracture strain		ISO 527-2	25 %
Bending modulus		ISO 178	2800 Mpa
Tensile strain	Yield	ISO 527-2	4.5 %
tensile strength	Yield	ISO 527-2	82.0 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	-- Mpa
Tensile creep modulus		1 hr	ISO 899-1	-- Mpa
impact performance	Test Condition	Test Method	DUPONT SINGAPORE/101L
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	400 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.5 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.5 kJ/m²
hardness	Test Condition	Test Method	DUPONT SINGAPORE/101L
Rockwell hardness	M -Sale	ISO 2039-2	79
Rockwell hardness		R -Sale	ISO 2039-2	121