PA66 R530H NT Q447 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA66 ASCEND USA R530H NT Q447

Enhanced level

US$ 3,530 / MT

FOB Dongguan Port

flammability	Test Condition	Test Method	ASCEND USA/R530H NT Q447
Burning wire flammability index	1.5mm	IEC 60695-2-12	675 °C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	700 °C
UL flame retardant rating	1.5mm	UL 94	HB
Burning wire flammability index	0.75mm	IEC 60695-2-12	675 °C
UL flame retardant rating	0.75mm	UL 94	HB
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	700 °C
UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	3.0mm	IEC 60695-2-12	675 °C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	700 °C
Physical properties	Test Condition	Test Method	ASCEND USA/R530H NT Q447
Water absorption rate	23°C,24hr	ISO 62	0.90 %
density		ISO 1183	1.37 g/cm³
Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.40 %
Water absorption rate	Equilibrium,50%RH	ISO 62	1.9 %
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	0.90 %
thermal performance	Test Condition	Test Method	ASCEND USA/R530H NT Q447
RTI Imp	3.0mm	UL 746	120 °C
Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO 11359-2	2.2E-05 cm/cm/°C
RTI Str	0.75mm	UL 746	125 °C
RTI Imp	1.5mm	UL 746	120 °C
RTI Elec	3.0mm	UL 746	140 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
RTI Str	3.0mm	UL 746	140 °C
Melting temperature		ISO 11357-3	260 °C
RTI Imp	0.75mm	UL 746	120 °C
RTI Str	1.5mm	UL 746	140 °C
Linear coefficient of thermal expansion	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260 °C
RTI Elec	1.5mm	UL 746	140 °C
RTI Elec		0.75mm	UL 746	140 °C
mechanical properties	Test Condition	Test Method	ASCEND USA/R530H NT Q447
bending strength	23°C	ISO 178	270 Mpa
Tensile modulus	23°C	ISO 527-2	10000 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
tensile strength	Break,23°C	ISO 527-2	195 Mpa
Bending modulus	23°C	ISO 178	9600 Mpa
Poisson's Ratio	23°C	ISO 527	0.40
Electrical performance	Test Condition	Test Method	ASCEND USA/R530H NT Q447
Volume resistivity	3.00mm	IEC 60093	1E+13 ohms·cm
Hot wire ignition	0.75mm	UL 746	PLC 4
High arc combustion index	3.0mm	UL 746	PLC 0
Hot wire ignition	1.5mm	UL 746	PLC 3
High arc combustion index	1.5mm	UL 746	PLC 0
Dielectric strength	1.00mm	IEC 60243	20 KV/mm
High arc combustion index	0.75mm	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Arc resistance	3.00mm	ASTM D495	PLC6
Hot wire ignition	3.0mm	UL 746	PLC 4
impact performance	Test Condition	Test Method	ASCEND USA/R530H NT Q447
Impact strength of cantilever beam gap	-30°C	ISO 180	10 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	10 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	65 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	11 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	12 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	75 kJ/m²