PA66 R530H NT Q447 ASCEND USA

Form：Granules | Grade：Enhanced level

Properties:

AntichemicalHydrolysis resistanceFatigue resistanceHigh mobility

Typical Applications:

GearsAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Gears \| Automotive sector
Properties:	Antichemical \| Hydrolysis resistance \| Fatigue resistance \| High mobility

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	75	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	12	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	65	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	700	°C
Hot filament ignition temperature	Hot filament ignition temperature	0.75mm	IEC 60695-2-13	700	°C
Burning wire flammability index	3.0mm	IEC 60695-2-12	675	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	675	°C
	Burning wire flammability index	Burning wire flammability index	0.75mm	IEC 60695-2-12	675	°C
UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	HB
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	700	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Poisson's Ratio	23°C	ISO 527	0.40
Tensile modulus	23°C	ISO 527-2	10000	Mpa
tensile strength	Break,23°C	ISO 527-2	195	Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0	%
Bending modulus	23°C	ISO 178	9600	Mpa
bending strength	23°C	ISO 178	270	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str	3.0mm	UL 746	140	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250	°C
Melting temperature		ISO 11357-3	260	°C
Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO 11359-2	2.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04	cm/cm/°C
RTI Elec	0.75mm	UL 746	140	°C
	RTI Elec	1.5mm	UL 746	140	°C
	RTI Elec	RTI Elec	3.0mm	UL 746	140	°C
RTI Imp	0.75mm	UL 746	120	°C
	RTI Imp	1.5mm	UL 746	120	°C
	RTI Imp	RTI Imp	3.0mm	UL 746	120	°C
RTI Str	0.75mm	UL 746	125	°C
RTI Str	RTI Str	1.5mm	UL 746	140	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.37	g/cm³
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	0.90	%
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.40	%
Water absorption rate	23°C,24hr	ISO 62	0.90	%
Water absorption rate	Water absorption rate	Equilibrium,50%RH	ISO 62	1.9	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition	3.0mm	UL 746	PLC 4
	Hot wire ignition	1.5mm	UL 746	PLC 3
	Hot wire ignition	Hot wire ignition	0.75mm	UL 746	PLC 4
High voltage arc tracing rate	HVTR	UL 746	PLC 1
High arc combustion index	3.0mm	UL 746	PLC 0
	High arc combustion index	1.5mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index	0.75mm	UL 746	PLC 0
Arc resistance	3.00mm	ASTM D495	PLC6
Dielectric strength	1.00mm	IEC 60243	20	KV/mm
Volume resistivity	3.00mm	IEC 60093	1E+13	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.