ABS POLYLAC® PA-757 TAIWAN CHIMEI
212
- Unit Price:
- $1806 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 557MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 130****13
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 1.6 | g/10min | |
| ASTM D1238/ISO 1133 | 23 | g/10min | ||
| Density | ASTM D792/ISO 1183 | 1.05 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | ASTM D638/ISO 527 | 490(6,950) | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | 20 | % | |
| Rockwell Hardness | ASTM D785 | R-116 | ||
| Flexural Modulus | ASTM D790/ISO 178 | 27000(38000) | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 790(11,660) | kg/cm²(MPa)[Lb/in²] | |
| Notched Izod Impact Strength | ASTM D256/ISO 179 | 20(3.7) | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 17(3.1) | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning Rate | UL94 | 1.6mmHB | ||
| Heat Deflection Temperature | ASTM D648/ISO 75 | 99(210) | ℃（℉） | |
| ASTM D648/ISO 75 | 88(190) | ℃（℉） | ||
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 105(221) | ℃（℉） |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying conditions | 80°C下烘料约2~3小时 | |||
| Processing (Melt) Temp | 180~220 | °C | ||
| 190~230 | °C | |||
| 180~230°C | °C | |||
| Mold Temperature | 30~70°C | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.