ABS POLYLAC®  PA-757 TAIWAN CHIMEI

465
  • Unit Price:
    $1626 USD/MT
  • Packaging Specification:
    25KG/PKG
  • Supply Quantity:
    20MT
  • Delivery Terms:
    FOB
  • Port of Loading:
    Huangpu port, China
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan East Asia Plastic Co., Ltd.

+86 138****46

1925********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical PropertiesTest ConditionTest MethodTest ResultUnit
DensityASTM D792/ISO 11831.05
Melt Mass-Flow RateASTM D1238/ISO 11331.6g/10min
Melt Mass-Flow RateASTM D1238/ISO 113323g/10min
Mechanical PropertiesTest ConditionTest MethodTest ResultUnit
Tensile StrengthASTM D638/ISO 527490(6,950)kg/cm²(MPa)[Lb/in²]
Tensile ElongationASTM D638/ISO 52720%
Rockwell HardnessASTM D785R-116
Flexural ModulusASTM D790/ISO 17827000(38000)kg/cm²(MPa)[Lb/in²]
Flexural StrengthASTM D790/ISO 178790(11,660)kg/cm²(MPa)[Lb/in²]
Izod notch impact strengthASTM D256/ISO 17920(3.7)kg·cm/cm(J/M)ft·lb/in
Izod notch impact strengthASTM D256/ISO 17917(3.1)kg·cm/cm(J/M)ft·lb/in
Thermal PropertiesTest ConditionTest MethodTest ResultUnit
Burning RateUL941.6mmHB
Deflection Temperature Under Load?ASTM D648/ISO 7599(210)℃(℉)
Deflection Temperature Under Load?ASTM D648/ISO 7588(190)℃(℉)
Vicat Softening TemperatureASTM D1525/ISO R306105(221)℃(℉)
ProcessingTest ConditionTest MethodTest ResultUnit
Drying conditions80°C下烘料约2~3小时
Mold Temperature30~70°C°C
Processing temperature180~220°C
Processing temperature190~230°C
Processing temperature180~230°C°C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.