PPS LNP™ LUBRICOMP™ OL-4030 SABIC INNOVATIVE US

345

Unit Price:US$ 10,030 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Carbon fiber reinforced｜High impact resistance
Application Areas:Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	4.8	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	2.2	kJ/m²
Multi axis Instrumented Impact Energy		ISO 6603-2	0.400	J
Dart impact	23°C,TotalEnergy	ASTM D3763	1.00	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ISO 527-2/5	20.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	21.0	Mpa
Tensile modulus		ISO 527-2/1	3370	Mpa
Tensile modulus	Tensile modulus		ASTM D638	3590	Mpa
bending strength	Break,50.0mmSpan	ASTM D790	65.0	Mpa
bending strength	bending strength		ISO 178	56.0	Mpa
Bending modulus		ISO 178	3320	Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	3870	Mpa
Tensile strain	Break	ISO 527-2/5	0.60	%
elongation	Break	ASTM D638	0.60	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	6.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	6E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	109	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	108	°C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	178	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	175	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.040	%
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.020	%
Shrinkage rate	TD：24hr	ASTM D955	1.0-3.0	%
Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.90-2.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPS LNP™ LUBRICOMP™ OL-4030 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index