PC IUPILON™ EFR3000 MITSUBISHI ENGINEERING JAPAN
219
- Unit Price:US$ 2,283 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Flame retardant
- Application Areas:Non specific food
- Color:--
- Grade:Injection grade
Material Certification
TDS
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整 | ||
| characteristic | 磷含量低（-无）、无溴、阻燃性能 | ||
| Color | 不透明 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 137 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000067 mm/mm.℃ | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 137 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 125 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.7E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 6.0E+15 Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 3.10 | |
| volume resistivity | ASTM D257/IEC 60093 | 3.0E+16 Ω.cm | |
| Dielectric loss | ASTM D150/IEC 60250 | 0.00060 | |
| ASTM D150/IEC 60250 | 0.0090 | ||
| Surface Resistivity | IEC 60093 | 6E+15 ohms | |
| volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| dielectric strength | 1.00mm | IEC 60243-1 | 31 KV/mm |
| 3.00mm | IEC 60243-1 | 18 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.10 |
| 1MHz | IEC 60250 | 3.10 | |
| Dissipation Factor | 100Hz | IEC 60250 | 6E-04 |
| 1MHz | IEC 60250 | 9E-03 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.24 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 22 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 21.0 cm3/10min |
| shrinkage rate | TD:3.20mm | 0.50-0.70 % | |
| MD:3.20mm | 0.50-0.70 % | ||
| 吸水率(饱和,23°C) | 0.24 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at break | ASTM D638/ISO 527 | 4.7 % | |
| Tensile modulus | ASTM D638/ISO 527 | 2300 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 61.0 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 2500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 92.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 61.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.7 % |
| Nominal tensile fracture strain | ISO 527-2 | 67 % | |
| flexural modulus | ISO 178 | 2500 Mpa | |
| bending strength | ISO 178 | 92.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.