PC EFR3000 MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Non specific food
High mobility、Flame retardant
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
Surface ResistivityASTM D257/IEC 600936.0E+15 Ω
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600933E+16 ohms·cm
dielectric constantASTM D150/IEC 602503.10
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
Dielectric lossASTM D150/IEC 602500.0090
dielectric strength3.00mmIEC 60243-118 KV/mm
relative permittivity1MHzIEC 602503.10
Volume resistivityASTM D257/IEC 600933.0E+16 Ω.cm
Surface ResistivityIEC 600936E+15 ohms
Dissipation Factor1MHzIEC 602509E-03
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
bending strengthASTM D790/ISO 17892.0 kg/cm²(MPa)[Lb/in²]
Tensile modulusISO 527-22300 Mpa
Flexural modulusASTM D790/ISO 1782500 kg/cm²(MPa)[Lb/in²]
Nominal tensile fracture strainISO 527-267 %
bending strengthISO 17892.0 Mpa
Flexural modulusISO 1782500 Mpa
Tensile strain屈服ISO 527-24.7 %
Tensile modulusASTM D638/ISO 5272300 kg/cm²(MPa)[Lb/in²]
elongation at breakASTM D638/ISO 5274.7 %
tensile strength 屈服ISO 527-261.0 Mpa
ASTM D638/ISO 52761.0 kg/cm²(MPa)[Lb/in²]
otherTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
characteristic磷含量低（-无）、无溴、阻燃性能
notes以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整
Color不透明
Physical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
Shrinkage rateASTM D9550.50-0.70 %
Water absorption rateASTM D570/ISO 620.24 %
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
UL flame retardant rating1.0mmUL 94V-0
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
Shrinkage rateTD:3.20mm0.50-0.70 %
Melt volume flow rate300°C/1.2kgISO 113321.0 cm3/10min
Shrinkage rate吸水率(饱和,23°C)0.24 %
MD:3.20mm0.50-0.70 %
melt mass-flow rate300°C/1.2kgISO 113322 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000
Heat distortion temperatureHDTASTM D648/ISO 75137 ℃（℉）
0.45MPa,未退火，HDTISO 75-2/B137 °C
1.8MPa,未退火，HDTISO 75-2/A125 °C
Linear coefficient of thermal expansionMDISO 11359-26.6E-05 cm/cm/°C
TDISO 11359-26.7E-05 cm/cm/°C
ASTM D696/ISO 113590.000067 mm/mm.℃