PC/PBT XENOY™ 5220-BK1066 SABIC INNOVATIVE US
337
- Unit Price:US$ 3,063 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:133MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Low warpage
- Application Areas:Automotive Applications｜Casters｜Plastic bag
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 75.0 °C |
| vicat | ASTM D152512 | 122 °C | |
| -- | ISO 306/B50 | 120 °C | |
| -- | ISO 306/B120 | 125 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 9.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 9.5E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 9E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 75.0 °C | |
| RTI Imp | UL 746 | 75.0 °C | |
| RTI Str | UL 746 | 75.0 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 107 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 84.0 °C | |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 99.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 55 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 30 kJ/m² |
| 23°C | ISO 180/1A | 50 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 250°C/5.0kg | ISO 1133 | 16 g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 15.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.80-1.0 % |
| TD2 | 内部方法 | 0.80-1.0 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % | |
| Outdoor applicability | UL 746C | f2 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Break | ASTM D638 | 51.0 Mpa |
| 断裂 | ISO 527-2/50 | 50.0 Mpa | |
| Tensile strain | Yield | ASTM D638 | 4.0 % |
| 屈服 | ISO 527-2/50 | 4.0 % | |
| Break | ASTM D638 | 120 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2030 Mpa |
| ISO 178 | 2000 Mpa | ||
| bending strength | ISO 178 | 80.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 84.0 Mpa | |
| Tensile modulus | --3 | ASTM D638 | 2250 Mpa |
| --4 | ASTM D638 | 2250 Mpa | |
| ISO 527-2/1 | 2050 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 53.0 Mpa |
| 屈服 | ISO 527-2/50 | 50.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.