PA66 Leona™ FG171 ASAHI JAPAN

291

Unit Price:US$ 4,850 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
79.8MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Electrical applications｜switch｜Hose
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	67	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-0
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break,23°C	ISO 527-2	2.5	%
elongation	Break	ASTM D638	2.5	%
tensile strength	Break,23°C	ISO 527-2	154	Mpa
tensile strength	tensile strength		ASTM D638	162	Mpa
Tensile modulus	23°C	ISO 527-2	10200	Mpa
bending strength	23°C	ISO 178	244	Mpa
bending strength	bending strength		ASTM D790	256	Mpa
Bending modulus	23°C	ISO 178	9700	Mpa
Bending modulus	Bending modulus		ASTM D790	8900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	256	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	250	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	240	°C
Linear coefficient of thermal expansion	MD	ASTM D696	3E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	255	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	--	%
Shrinkage rate	吸水率(Saturation,23°C)	Internal Method	--	%
	Shrinkage rate	MD	Internal Method	0.40	%
	Shrinkage rate	Shrinkage rate	TD	Internal Method	0.90	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 2
Surface resistivity		ASTM D257	1E+14	ohms
Surface resistivity	Surface resistivity		IEC 60093	1E+14	ohms
Dielectric strength		IEC 60243-1	28	KV/mm
Dielectric strength	Dielectric strength		ASTM D149	28	KV/mm
Volume resistivity	23°C	IEC 60093	1E+15	ohms·cm
Volume resistivity	Volume resistivity		ASTM D257	1E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	95
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 Leona™ FG171 ASAHI JAPAN

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index