PA66 FG171 ASAHI JAPAN
Leona™ 
Electrical applications,switch,Hose
Glass fiber reinforced,Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodASAHI JAPAN/FG171
Impact strength of simply supported beam without notchISO 17967 kJ/m²
hardnessTest ConditionTest MethodASAHI JAPAN/FG171
Rockwell hardnessM级ASTM D78595
M级ISO 2039-295
Electrical performanceTest ConditionTest MethodASAHI JAPAN/FG171
Compared to the Leakage Tracking Index (CTI)3.00mmIEC 60112PLC 2
Volume resistivityASTM D2571E+15 ohms·cm
dielectric strengthIEC 60243-128 KV/mm
Surface ResistivityASTM D2571E+14 ohms
Volume resistivity23°CIEC 600931E+15 ohms·cm
dielectric strengthASTM D14928 KV/mm
Surface ResistivityIEC 600931E+14 ohms
Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/FG171
elongation断裂ASTM D6382.5 %
Tensile strain断裂,23°CISO 527-22.5 %
bending strength23°CISO 178244 Mpa
ASTM D790256 Mpa
Flexural modulus23°CISO 1789700 Mpa
Tensile modulus23°CISO 527-210200 Mpa
tensile strength 断裂,23°CISO 527-2154 Mpa
Flexural modulusASTM D7908900 Mpa
tensile strength ASTM D638162 Mpa
flammabilityTest ConditionTest MethodASAHI JAPAN/FG171
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
UL flame retardant rating0.75mmUL 94V-0
physical property Test ConditionTest MethodASAHI JAPAN/FG171
Shrinkage rateMD内部方法0.40 %
Water absorption rate平衡,23°C,50%RHISO 62-- %
Shrinkage rate吸水率(饱和,23°C)内部方法-- %
TD内部方法0.90 %
Thermal performanceTest ConditionTest MethodASAHI JAPAN/FG171
Heat distortion temperature1.8MPa,未退火，HDTASTM D648250 °C
0.45MPa,未退火，HDTASTM D648255 °C
0.45MPa,未退火，HDTISO 75-2/B256 °C
1.8MPa,未退火，HDTISO 75-2/A240 °C
Linear coefficient of thermal expansionMDASTM D6963E-05 cm/cm/°C