PPA

PPA AMODEL® AT-1116HS SOLVAY USA

258

Unit Price:US$ 11,983 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Filler: Glass fiber reinforced material｜16% filler by weight
Application Areas:Electrical applications｜Spool｜Laptop case｜Parts under the hood of a car｜bearing｜Machine/mechanical components｜Industrial applications｜Application in the automotive field｜Metal substitution｜Industrial components｜currency｜Vehicle electronics
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	TotalEnergy	ASTM D3763	10.0 J
	Dart impact	EnergyatMaxumumLoad3	ASTM D3763	-- J
	Dart impact	Dart impact	EnergyatMaxumumLoad2	ASTM D3763	1.76 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	53 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	86 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
shear strength		ASTM D732	69.6 Mpa
compressive strength		ASTM D695	124 Mpa
bending strength	100°C	ISO 178	141 Mpa
	bending strength	23°C	ISO 178	197 Mpa
	bending strength	bending strength		ASTM D790	226 Mpa
Bending modulus	100°C	ISO 178	4960 Mpa
	Bending modulus	23°C	ISO 178	6690 Mpa
	Bending modulus	Bending modulus		ASTM D790	6000 Mpa
Tensile strain	Break,24°C	ISO 527-2	4.2 %
Tensile strain	Tensile strain	Break,23°C	ISO 527-2	3.7 %
elongation	Break	ASTM D638	3.8 %
tensile strength	Break,24°C	ISO 527-2	65.5 Mpa
	tensile strength	Break,23°C	ISO 527-2	160 Mpa
	tensile strength	tensile strength		ASTM D638	161 Mpa
Tensile modulus	100°C	ISO 527-2	6690 Mpa
	Tensile modulus	23°C	ISO 527-2	6890 Mpa
	Tensile modulus	Tensile modulus		ASTM D638	6480 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Annealed	ASTM D648	268 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	258 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ASTM D648	254 °C
Melting temperature		ASTM D3418	310 °C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2.2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	7.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1.2E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr	ASTM D570	0.20 %
Shrinkage rate	TD	ASTM D955	0.60 %
Shrinkage rate	Shrinkage rate	MD	ASTM D955	0.60 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.