PPA AT-1116HS SOLVAY USA
AMODEL®
Electrical applications、Spool、Laptop case、Parts under the hood of a、bearing、Machine/mechanical compon、Industrial applications、Application in the automo、Metal substitution、Industrial components、currency、Vehicle electronics
High temperature resistan、Filler: Glass fiber reinf、16% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SOLVAY USA/AT-1116HS |
---|---|---|---|
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 53 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 86 kJ/m² |
Dart impact | TotalEnergy | ASTM D3763 | 10.0 J |
EnergyatMaxumumLoad3 | ASTM D3763 | -- J | |
EnergyatMaxumumLoad2 | ASTM D3763 | 1.76 J |
Mechanical properties | Test Condition | Test Method | SOLVAY USA/AT-1116HS |
---|---|---|---|
bending strength | ASTM D790 | 226 Mpa | |
Flexural modulus | 100°C | ISO 178 | 4960 Mpa |
Tensile modulus | 23°C | ISO 527-2 | 6890 Mpa |
tensile strength | 断裂,23°C | ISO 527-2 | 160 Mpa |
断裂,24°C | ISO 527-2 | 65.5 Mpa | |
Tensile modulus | 100°C | ISO 527-2 | 6690 Mpa |
Flexural modulus | ASTM D790 | 6000 Mpa | |
tensile strength | ASTM D638 | 161 Mpa | |
Tensile strain | 断裂,24°C | ISO 527-2 | 4.2 % |
Tensile modulus | ASTM D638 | 6480 Mpa | |
bending strength | 100°C | ISO 178 | 141 Mpa |
elongation | 断裂 | ASTM D638 | 3.8 % |
Tensile strain | 断裂,23°C | ISO 527-2 | 3.7 % |
bending strength | 23°C | ISO 178 | 197 Mpa |
Flexural modulus | 23°C | ISO 178 | 6690 Mpa |
shear strength | ASTM D732 | 69.6 Mpa | |
compressive strength | ASTM D695 | 124 Mpa |
physical property | Test Condition | Test Method | SOLVAY USA/AT-1116HS |
---|---|---|---|
Shrinkage rate | MD | ASTM D955 | 0.60 % |
Water absorption rate | 24hr | ASTM D570 | 0.20 % |
Shrinkage rate | TD | ASTM D955 | 0.60 % |
Thermal performance | Test Condition | Test Method | SOLVAY USA/AT-1116HS |
---|---|---|---|
Linear coefficient of thermal expansion | TD:100到200°C | ASTME831 | 1.2E-04 cm/cm/°C |
Heat distortion temperature | 1.8MPa,退火,HDT | ASTM D648 | 254 °C |
Linear coefficient of thermal expansion | MD:100到200°C | ASTME831 | 1.6E-05 cm/cm/°C |
TD:0to100°C | ASTME831 | 7.5E-05 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 258 °C |
melting temperature | ASTM D3418 | 310 °C | |
Heat distortion temperature | 0.45MPa,退火,HDT | ASTM D648 | 268 °C |
Linear coefficient of thermal expansion | MD:0to100°C | ASTME831 | 2.2E-05 cm/cm/°C |