PA6 Durethan®  DP BKV 60 H2.0 EF 900116 LANXESS GERMANY

411
  • Unit Price:US$ 4,275 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    75MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Filler: Glass fiber reinforced material60% filler by weight
  • Application Areas:--
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Multi axis Instrumented Peak Impact Force-30°CISO 6603-21350 N
Multi axis Instrumented Impact Energy23°CISO 6603-24.30 J
Multi axis Instrumented Impact Energy-30°CISO 6603-23.80 J
Multi axis Instrumented Peak Impact Force23°CISO 6603-21480 N
Suspended wall beam without notch impact strength23°CISO 180/1U90 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U95 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU95 kJ/m²
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthBreak,23°CISO 527-2/5230 Mpa
Tensile modulus23°CISO 527-2/119400 Mpa
Bending strain23°CISO 178/A3.0 %
bending strength23°C4ISO 178/A390 Mpa
bending strength3.5%Strain,23°CISO 178/A-- Mpa
Bending modulus23°CISO 178/A20000 Mpa
Tensile strainBreak,23°CISO 527-2/52.5 %
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionMD:23to55°CISO 11359-21E-05 cm/cm/°C
Melting temperatureISO 11357-3221 °C
Hot deformation temperature8.0MPa,UnannealedISO 75-2/C186 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A213 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B220 °C
Linear coefficient of thermal expansionTD:23to55°CISO 11359-28E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateTD:280°C,2.00mm2ISO 25770.60 %
Shrinkage rateTD:120°C,4hr,2.00mm3ISO 25770.020 %
Shrinkage rateMD:280°C,2.00mm2ISO 25770.30 %
Water absorption rateEquilibrium,23°C,50%RHISO 621.2 %
Water absorption rateSaturation,23°CISO 623.8 %
Shrinkage rateMD:120°C,4hr,2.00mm3ISO 25770.030 %
Supplementary InformationTest ConditionTest MethodTest Result
ISO ShortcutISO 1874PA6.GHR.10-190.GF60
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.