PA6 DP BKV 60 H2.0 EF 900116 LANXESS GERMANY
Durethan®
--
Filler: Glass fiber reinf、60% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | LANXESS GERMANY/DP BKV 60 H2.0 EF 900116 |
---|---|---|---|
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 95 kJ/m² |
23°C | ISO 180/1U | 90 kJ/m² | |
Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 3.80 J |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 95 kJ/m² |
Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 1480 N |
Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 4.30 J |
Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 1350 N |
Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/DP BKV 60 H2.0 EF 900116 |
---|---|---|---|
ISO Shortcut | ISO 1874 | PA6.GHR.10-190.GF60 |
Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/DP BKV 60 H2.0 EF 900116 |
---|---|---|---|
Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.5 % |
Flexural modulus | 23°C | ISO 178/A | 20000 Mpa |
tensile strength | 断裂,23°C | ISO 527-2/5 | 230 Mpa |
Bending Strain | 23°C | ISO 178/A | 3.0 % |
bending strength | 3.5%Strain,23°C | ISO 178/A | -- Mpa |
Tensile modulus | 23°C | ISO 527-2/1 | 19400 Mpa |
bending strength | 23°C4 | ISO 178/A | 390 Mpa |
physical property | Test Condition | Test Method | LANXESS GERMANY/DP BKV 60 H2.0 EF 900116 |
---|---|---|---|
Shrinkage rate | MD:120°C,4小时,2.00mm3 | ISO 2577 | 0.030 % |
TD:280°C,2.00mm2 | ISO 2577 | 0.60 % | |
MD:280°C,2.00mm2 | ISO 2577 | 0.30 % | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.2 % |
饱和,23°C | ISO 62 | 3.8 % | |
Shrinkage rate | TD:120°C,4小时,2.00mm3 | ISO 2577 | 0.020 % |
Thermal performance | Test Condition | Test Method | LANXESS GERMANY/DP BKV 60 H2.0 EF 900116 |
---|---|---|---|
melting temperature | ISO 11357-3 | 221 °C | |
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 1E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 220 °C |
Linear coefficient of thermal expansion | TD:23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 213 °C |
8.0MPa,未退火,HDT | ISO 75-2/C | 186 °C |