POM Iupital™ F30-03 MITSUBISHI THAILAND
335
- Unit Price:US$ 2,165 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:249.3MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Thermal stability｜wear resistant｜High rigidity｜High impact resistance｜currency
- Application Areas:Thin walled products
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 2.0 % | ||
| Water absorption rate | ISO 62 | 0.22 % | |
| density | ISO 1183 | 1.41 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 27 g/10min | |
| Melt volume flow rate | ISO 1133 | 23.0 cm3/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2900 Mpa | |
| tensile strength | ISO 527-2 | 64.0 Mpa | |
| Tensile strain | ISO 527-2 | 7.5 % | |
| Nominal tensile fracture strain | ISO 527-2 | 25 % | |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| bending strength | ISO 178 | 91.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 6.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 150 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| relative permittivity | IEC 60250 | 3.90 | |
| Dissipation Factor | IEC 60250 | 2E-03 | |
| IEC 60250 | 7E-03 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| IEC 60243-1 | 19 KV/mm | ||
| relative permittivity | IEC 60250 | 3.90 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 156 °C | |
| ISO 75-2/A | 100 °C | ||
| melting temperature | ISO 11357-3 | 166 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| ISO 11359-2 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.