POM F30-03 MITSUBISHI THAILAND
Iupital™
Thin walled products
High mobility、Thermal stability、wear resistant、High rigidity、High impact resistance、currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI THAILAND/F30-03 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 150 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/F30-03 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2900 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 25 % | |
| bending strength | ISO 178 | 91.0 Mpa | |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 7.5 % |
| tensile strength | 屈服 | ISO 527-2 | 64.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/F30-03 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | 1.00mm | IEC 60243-1 | 32 KV/mm |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
| relative permittivity | 100Hz | IEC 60250 | 3.90 |
| dielectric strength | 3.00mm | IEC 60243-1 | 19 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.90 |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 7E-03 |
| flammability | Test Condition | Test Method | MITSUBISHI THAILAND/F30-03 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/F30-03 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 23.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.22 % |
| density | ISO 1183 | 1.41 g/cm³ | |
| Shrinkage rate | MD：3.00mm | 2.0 % | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 27 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/F30-03 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 156 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |