PBT/ASA

PBT/ASA POLYFORT® A3GF20 A SCHULMAN USA

412

Unit Price:US$ 3,073 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
43MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low warpage｜Excellent surface finish｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	30 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	3.0mm	IEC 60695-2-12	700 °C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	725 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725 °C
Burning rate	2.00mm	ISO 3795	20 mm/min
Flammability level	1.5mm	IEC 60695-11-10,-20	HB
Flammability level	Flammability level	3.0mm	IEC 60695-11-10,-20	HB
Burning wire flammability index	1.5mm	IEC 60695-2-12	700 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	6500 Mpa
tensile strength	Break	ISO 527-2/1A/5	96.0 Mpa
Tensile strain	Break	ISO 527-2/1A/5	2.6 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	210 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	172 °C
Vicat softening temperature	--	ISO 306/A50	205 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	20.0 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionA	IEC 60112	V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT/ASA POLYFORT® A3GF20 A SCHULMAN USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet