Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT/ASA A3GF20 A SCHULMAN USA
POLYFORT®
--
Low warpage、Excellent surface finish、Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/A3GF20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| -30°C | ISO 179/1eU | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | A SCHULMAN USA/A3GF20 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/A3GF20 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 6500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 96.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.6 % |
| flammability | Test Condition | Test Method | A SCHULMAN USA/A3GF20 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 725 °C |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 700 °C |
| burning rate | 2.00mm | ISO 3795 | 20 mm/min |
| Flammability level | 3.0mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 725 °C |
| physical property | Test Condition | Test Method | A SCHULMAN USA/A3GF20 |
|---|---|---|---|
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 20.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/A3GF20 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 172 °C |
| vicat | -- | ISO 306/A50 | 205 °C |
| -- | ISO 306/B50 | 145 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 210 °C |