Material Description
- Material Properties:Flame retardant
- Application Areas:Electrical appliances
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale,3.20mm,Injection | ASTM D785 | 123 |
| R-Sale,4.00mm | ISO 2039-2 | 123 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 139 °C |
| 1.8MPa,Unannealed | ASTM D648 | 127 °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 125 °C | |
| Vicat softening temperature | -- | ASTM D15256 | 149 °C |
| -- | ISO 306/A120 | 150 °C | |
| -- | ISO 306/B50 | 144 °C | |
| Ball pressure temperature | IEC 60335-1 | >125 °C | |
| Linear coefficient of thermal expansion | MD：-22to85°C | ASTM D696 | 6.5E-05 cm/cm/°C |
| RTI Elec | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 125 °C | |
| RTI | UL 746 | 125 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 960 °C |
| Extreme Oxygen Index | ASTMD2863 | 35 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| MD | ISO 294-4 | 0.50-0.70 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Bending modulus | 4.00mm,Injection4 | ISO 178 | 2400 Mpa |
| bending strength | 3.20mm,Injection | ASTM D790 | 93.8 Mpa |
| 4.00mm,Injection4 | ISO 178 | 94.0 Mpa | |
| Tensile modulus | 3.20mm,Injection | ASTM D638 | 2210 Mpa |
| 4.00mm,Injection | ISO 527-2/50 | 2200 Mpa | |
| tensile strength | Yield,3.20mm,Injection3 | ASTM D638 | 60.0 Mpa |
| Yield,4.00mm,Injection | ISO 527-2/50 | 60.0 Mpa | |
| Break,3.20mm,Injection | ASTM D638 | 57.9 Mpa | |
| Break,4.00mm,Injection | ISO 527-2/50 | 58.0 Mpa | |
| elongation | Yield,3.20mm,Injection | ASTM D638 | 6.2 % |
| Yield,4.00mm,Injection | ISO 527-2/50 | 6.0 % | |
| Break,3.20mm,Injection | ASTM D638 | 110 % | |
| Break,4.00mm,Injection | ISO 527-2/50 | 110 % | |
| Bending modulus | 3.20mm,Injection | ASTM D790 | 2400 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,3.20mm,总能量 | ASTM D3763 | 58.8 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.