Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 8600-10 HC880055 STYRON TAIWAN
EMERGE™
Electrical appliances
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | STYRON TAIWAN/8600-10 HC880055 |
|---|---|---|---|
| Dart impact | 23°C,3.20mm,总能量 | ASTM D3763 | 58.8 J |
| hardness | Test Condition | Test Method | STYRON TAIWAN/8600-10 HC880055 |
|---|---|---|---|
| Rockwell hardness | R级,3.20mm,注塑 | ASTM D785 | 123 |
| R计秤,4.00mm | ISO 2039-2 | 123 |
| Mechanical properties | Test Condition | Test Method | STYRON TAIWAN/8600-10 HC880055 |
|---|---|---|---|
| Tensile modulus | 4.00mm,注塑 | ISO 527-2/50 | 2200 Mpa |
| tensile strength | 屈服,3.20mm,注塑3 | ASTM D638 | 60.0 Mpa |
| Flexural modulus | 4.00mm,注塑4 | ISO 178 | 2400 Mpa |
| elongation | 屈服,3.20mm,注塑 | ASTM D638 | 6.2 % |
| Flexural modulus | 3.20mm,注塑 | ASTM D790 | 2400 Mpa |
| elongation | 断裂,4.00mm,注塑 | ISO 527-2/50 | 110 % |
| tensile strength | 屈服,4.00mm,注塑 | ISO 527-2/50 | 60.0 Mpa |
| Tensile modulus | 3.20mm,注塑 | ASTM D638 | 2210 Mpa |
| elongation | 断裂,3.20mm,注塑 | ASTM D638 | 110 % |
| 屈服,4.00mm,注塑 | ISO 527-2/50 | 6.0 % | |
| bending strength | 4.00mm,注塑4 | ISO 178 | 94.0 Mpa |
| tensile strength | 断裂,4.00mm,注塑 | ISO 527-2/50 | 58.0 Mpa |
| 断裂,3.20mm,注塑 | ASTM D638 | 57.9 Mpa | |
| bending strength | 3.20mm,注塑 | ASTM D790 | 93.8 Mpa |
| flammability | Test Condition | Test Method | STYRON TAIWAN/8600-10 HC880055 |
|---|---|---|---|
| Limiting Oxygen Index | ASTMD2863 | 35 % | |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | STYRON TAIWAN/8600-10 HC880055 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| MD | ISO 294-4 | 0.50-0.70 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON TAIWAN/8600-10 HC880055 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 127 °C |
| 0.45MPa,未退火，HDT | ASTMD648 | 139 °C | |
| Ball pressure temperature | IEC 60335-1 | >125 °C | |
| vicat | -- | ISO 306/A120 | 150 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 125 °C |
| vicat | -- | ISO 306/B50 | 144 °C |
| -- | ASTM D15256 | 149 °C | |
| Linear coefficient of thermal expansion | MD：-22到85°C | ASTM D696 | 6.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 125 °C | |
| RTI | UL 746 | 125 °C | |
| RTI Elec | UL 746 | 125 °C |