PBT/F/PTFE

PBT/F/PTFE LNP™ LUBRICOMP™ WFL-4036 NAT SABIC INNOVATIVE US

256

Unit Price:US$ 8,515 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Aging resistance
Application Areas:Automotive components｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.2 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	43 kJ/m²
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	13.7 J
Multi axis Instrumented Impact Energy		ISO 6603-2	2.61 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	10300 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	10600 Mpa
tensile strength	Break	ASTM D638	118 Mpa
tensile strength	tensile strength	Break	ISO 527-2	118 Mpa
elongation	Break	ASTM D638	2.3 %
Tensile strain	Break	ISO 527-2	2.2 %
Bending modulus		ASTM D790	10200 Mpa
Bending modulus	Bending modulus		ISO 178	10000 Mpa
bending strength		ASTM D790	193 Mpa
bending strength	bending strength		ISO 178	187 Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.57
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.41
Wear factor	Washer	ASTM D3702Modified	42.0 10^-10in^5-min/ft-lb-hr

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	218 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	214 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	3.9E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6.7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr,50%RH	ASTM D570	0.040 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.040 %
Shrinkage rate	MD：24hr	ASTM D955	0.10-0.30 %
	Shrinkage rate	TD：24hr	ASTM D955	0.50-1.0 %
		Shrinkage rate	TD:24hr	ISO 294-4	0.50-1.0 %
		Shrinkage rate	Shrinkage rate	MD:24hr	ISO 294-4	0.10-0.30 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT/F/PTFE LNP™ LUBRICOMP™ WFL-4036 NAT SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet