ABS/PMMA STAREX® SF-0950 BK Samsung Cheil South Korea

520

Unit Price:US$ 2,111 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜Easy to color
Application Areas:Automotive Applications｜Car dashboard｜Electronic and electrical enclosure｜Office equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	110 J/m
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	98 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ASTM D790	2600 Mpa
Bending modulus	Bending modulus		ISO 178	2700 Mpa
bending strength		ASTM D790	74.0 Mpa
bending strength	bending strength		ISO 178	85.0 Mpa
Tensile strain	Break	ISO 527-2/50	20 %
elongation	Break	ASTM D638	25 %
tensile strength	Break	ISO 527-2/50	40.0 Mpa
	tensile strength	Break	ASTM D638	34.0 Mpa
		tensile strength	Yield	ISO 527-2/50	55.0 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	51.0 Mpa
Tensile modulus		ISO 527-2/50	2600 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2500 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306/B50	100 °C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	78.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	92.0 °C
		Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	91.0 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	98.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD：3.20mm	ASTM D955	0.31-0.38 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.29-0.36 %
melt mass-flow rate	220°C/10.0kg	ISO 1133	13 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	13 g/10min
density		ISO 1183	1.10 g/cm³
density	density		ASTM D792	1.10 g/cm³
Shrinkage rate	MD:3.20mm	ISO 2577	0.29-0.36 %
Shrinkage rate	Shrinkage rate	TD:3.20mm	ISO 2577	0.31-0.38 %

hardness	Test Condition	Test Method	Test Result
Pencil hardness		JISK5401	H
Rockwell hardness	R-Scale	ASTM D785	116
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	116

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS/PMMA STAREX® SF-0950 BK Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet