ABS/PMMA SF-0950 BK Samsung Cheil South Korea
STAREX®
Automotive Applications、Car dashboard、Electronic and electrical、Office equipment
High gloss、Easy to color
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/SF-0950 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 98 J/m |
| 23°C | ISO 180/1A | 9.0 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 110 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/SF-0950 BK |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 116 |
| R级 | ASTM D785 | 116 | |
| Hardness | JISK5401 | H |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/SF-0950 BK |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2500 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| elongation | 断裂 | ASTM D638 | 25 % |
| Tensile modulus | ISO 527-2/50 | 2600 Mpa | |
| bending strength | ISO 178 | 85.0 Mpa | |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| bending strength | ASTM D790 | 74.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 34.0 Mpa |
| 屈服 | ASTM D638 | 51.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| Flexural modulus | ASTM D790 | 2600 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 40.0 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/SF-0950 BK |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/SF-0950 BK |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.29-0.36 % |
| TD:3.20mm | ISO 2577 | 0.31-0.38 % | |
| TD：3.20mm | ASTM D955 | 0.31-0.38 % | |
| density | ASTM D792 | 1.10 g/cm³ | |
| ISO 1183 | 1.10 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 13 g/10min |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.29-0.36 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/SF-0950 BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 78.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 92.0 °C | |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 91.0 °C | |
| vicat | ISO 306/B50 | 100 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 98.0 °C |