Material Description

Material Properties:Medium viscosity
Application Areas:film
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
RSV - Formic Acid, 1g/100ml		Internal Method	3.03
Puncture resistance		Internal Method	13.0 J/cm
Average Specific Heat Capacity	20 to 150°C		2250 J/kg/°C
Melt viscosity	260°C	Internal Method	810000 mPa·s

optical performance	Test Condition	Test Method	Test Result
Clarity		Internal Method	83 %

squeeze out	Test Condition	Test Method	Test Result
Traction roller			110 °C
Oral mold temperature			270 °C
Temperature in Zone 4 of the material cylinder			270 °C
Temperature in Zone 3 of the material cylinder			270 °C
Temperature in Zone 2 of the material cylinder			270 °C
Temperature in Zone 1 of the material cylinder			270 °C

mechanical properties	Test Condition	Test Method	Test Result
Friction coefficient	Static	ISO 8295	1.2
Friction coefficient	Friction coefficient	Dynamic	ISO 8295	1.0

thermal performance	Test Condition	Test Method	Test Result
Specific heat capacity			1550 J/kg/°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	9.0E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Stickiness		ISO 307	196 cm³/g

film	Test Condition	Test Method	Test Result
Oxygen permeability	85% RH : 23°C	ASTM D256A	38 cm³/m²/bar/24 hr
Oxygen permeability	Oxygen permeability	0% RH : 23°C	ASTM D256A	26 cm³/m²/bar/24 hr
Water vapor permeability	23°C, 85% RH	DIS 15106-1/-3	35 g/m²/24 hr
Trouser Tear - Parallel		ISO 6383-1	32.0
elongation	Break， MD	ISO 527-3	350 %
Tensile stress	Break，MD	ISO 527-3	82.0 Mpa
Tensile stress	Tensile stress	Yield，MD	ISO 527-3	31.0 Mpa
Tensile modulus		Internal Method	455 Mpa
Film thickness - tested			50 µm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Akulon® F130-C DSM HOLAND

Material Description

Technical Data Sheet Compare

Technical Data Sheet