PEI ULTEM™ HU2200-1H1000 SABIC INNOVATIVE US

422

Unit Price:US$ 11,410 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Food contact｜Filler: Glass fiber reinforced material｜20%｜Filler by weight
Application Areas:Wear resistant accessories｜chip｜Medical/nursing supplies｜medicine
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	8.00	J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	70	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	64	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,50.0mmSpan	ASTM D790	225	Mpa
bending strength	bending strength		ISO 178	228	Mpa
Bending modulus		ISO 178	6890	Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	6850	Mpa
Tensile strain	Break	ISO 527-2/5	4.0	%
elongation	Break	ASTM D638	4.0	%
Tensile strain	Yield	ISO 527-2/5	4.0	%
elongation	Yield	ASTM D638	4.0	%
tensile strength	Break	ISO 527-2/5	131	Mpa
	tensile strength	Break	ASTM D638	131	Mpa
		tensile strength	Yield	ISO 527-2/5	131	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	131	Mpa
Tensile modulus		ISO 527-2/1	6890	Mpa
Tensile modulus	Tensile modulus		ASTM D638	6890	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to150°C	ISO 11359-2	5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to150°C	ASTME831	5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：23to150°C	ISO 11359-2	2.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-20to150°C	ASTME831	2.5E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	218	°C
	Vicat softening temperature	--	ISO 306/B50	212	°C
	Vicat softening temperature	Vicat softening temperature		ASTM D152510	220	°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	205	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	208	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	337°C/6.6kg	ASTM D1238	6.0	g/10min
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	7.00	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.30-0.50	%
Water absorption rate	Saturation,23°C	ISO 62	1.0	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.55	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PEI ULTEM™ HU2200-1H1000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index