Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI HU2200-1H1000 SABIC INNOVATIVE US
ULTEM™
Wear resistant accessorie、chip、Medical/nursing supplies、medicine
Flame retardant、Food contact、Filler: Glass fiber reinf、20%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HU2200-1H1000 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.00 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 70 kJ/m² |
| 23°C | ISO 180/1A | 64 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU2200-1H1000 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 6890 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 131 Mpa |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 4.0 % |
| tensile strength | 断裂 | ASTM D638 | 131 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 6850 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 131 Mpa |
| Tensile modulus | ASTM D638 | 6890 Mpa | |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 225 Mpa |
| ISO 178 | 228 Mpa | ||
| Flexural modulus | ISO 178 | 6890 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| tensile strength | 屈服 | ASTM D638 | 131 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HU2200-1H1000 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30-0.50 % |
| Melt volume flow rate | 360°C/5.0kg | ISO 1133 | 7.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.55 % |
| 饱和,23°C | ISO 62 | 1.0 % | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HU2200-1H1000 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 218 °C |
| Linear coefficient of thermal expansion | TD：23to150°C | ISO 11359-2 | 5E-05 cm/cm/°C |
| MD：-20to150°C | ASTME831 | 2.5E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 212 °C |
| ASTM D152510 | 220 °C | ||
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 205 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 208 °C | |
| Linear coefficient of thermal expansion | TD：-40to150°C | ASTME831 | 5E-05 cm/cm/°C |
| MD：23到150°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |