PCTG Tritan™ 6002 EASTMAN USA
368
- Unit Price:US$ 3,010 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:116.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜Hydrolysis resistance
- Application Areas:Electrical applications｜Household daily necessities
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 20 g/10 min | |
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.15 % | ||
| Transmittance | D1003 | 89% | |
| Total transmittance | D1003 | 91% | |
| gloss | D1003 | 0.3% |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| film temperature | 15-30℃(60-80℉) | ||
| drying temperature | 70℃(160℉) | ||
| Processing melting temperature | 230-280℃(450-530℉) | ||
| drying time | 6小时 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | D792 | 1.2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 60.0 Mpa | |
| elongation | ASTM D638 | 15 % | |
| D638 | 5% | ||
| D638 | 320% | ||
| Flexural modulus | D790 | 2000MPa(2.9×10 | |
| ISO 178 | 1850MPa | ||
| bending strength | ISO 178 | 65MPa | |
| Tensile modulus | ISO 527 | 1800MPa | |
| Impact resistance (perforation), energy @ maximum load | D3763 | 42 J(31 ft bf) | |
| D3763 | 48 J/m(35 ft bf) | ||
| Impact strength of cantilever beam gap | ISO 180 | 7.8kJ/m | |
| ISO 180 | 4.8kJ/m | ||
| Tensile stress | D638 | 47MPa（6900 psi） | |
| D638 | 51MPa（7400 psi） | ||
| tensile strength | ISO 527 | 47MPa | |
| ISO 527 | 46MPa | ||
| Rockwell hardness | D785 | 103 | |
| Impact strength of cantilever beam gap | D4812 | NB J/m(NB ft bf/in) | |
| D4812 | NB J/m(NB ft bf/in) | ||
| D256 | 80 J/m(1.5 ft bf/in) | ||
| D256 | 40 J/m(0.7 ft bf/in) | ||
| elongation | ISO 527 | 4% | |
| ISO 527 | 200% | ||
| tensile strength | D790 | 69MPa(10000 psi) |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 15 KV/mm |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature at the rear of the barrel | 265 to 275 °C | ||
| Temperature in the middle of the barrel | 280 to 290 °C | ||
| Spray nozzle temperature | 285 to 295 °C | ||
| Processing (melt) temperature | 280 to 290 °C | ||
| Temperature | 60 to 80 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 135 °C | |
| ASTM D648 | 125 °C | ||
| Bending temperature | D648 | 73℃(164℉) | |
| D648 | 65℃(149℉) |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.