Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PCTG 6002 EASTMAN USA
Tritan™
Electrical applications、Household daily necessiti
Chemical resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| density | D792 | 1.2 |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| Impact strength of cantilever beam gap | @-40℃(-40?H)，切口 | D256 | 40 J/m(0.7 ft bf/in) |
| elongation | @屈服 | ISO 527 | 4% |
| Rockwell hardness | R刻度 | D785 | 103 |
| Flexural modulus | ISO 178 | 1850MPa | |
| Tensile stress | @屈服 | D638 | 47MPa（6900 psi） |
| Tensile modulus | ISO 527 | 1800MPa | |
| tensile strength | 屈服 | D790 | 69MPa(10000 psi) |
| elongation | @断裂 | D638 | 320% |
| Flexural modulus | D790 | 2000MPa(2.9×10 | |
| tensile strength | @断裂 | ISO 527 | 46MPa |
| Impact strength of cantilever beam gap | @-40℃，切口 | ISO 180 | 4.8kJ/m |
| bending strength | ISO 178 | 65MPa | |
| elongation | 断裂 | ASTM D638 | 15 % |
| @断裂 | ISO 527 | 200% | |
| Impact strength of cantilever beam gap | @23℃(73?H)，切口 | D256 | 80 J/m(1.5 ft bf/in) |
| @23℃，切口 | ISO 180 | 7.8kJ/m | |
| Impact resistance (perforation), energy @ maximum load | @23℃(73℉) | D3763 | 42 J(31 ft bf) |
| Tensile stress | @断裂 | D638 | 51MPa（7400 psi） |
| Impact strength of cantilever beam gap | @23℃(73℉)，未切口 | D4812 | NB J/m(NB ft bf/in) |
| Impact resistance (perforation), energy @ maximum load | @-40℃(-40℉) | D3763 | 48 J/m(35 ft bf) |
| Impact strength of cantilever beam gap | @-40℃(-40℉)，未切口 | D4812 | NB J/m(NB ft bf/in) |
| tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
| elongation | @屈服 | D638 | 5% |
| tensile strength | @屈服 | ISO 527 | 47MPa |
| Electrical performance | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+16 ohms·cm | |
| dielectric strength | 2.00 mm | ASTM D149 | 15 KV/mm |
| flammability | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| UL flame retardant rating | 3.2 mm | UL 94 | V-2 |
| processability | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| drying temperature | 70℃(160℉) | ||
| film temperature | 15-30℃(60-80℉) | ||
| Processing melting temperature | 230-280℃(450-530℉) | ||
| drying time | 6小时 |
| physical property | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| gloss | D1003 | 0.3% | |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Total transmittance | D1003 | 91% | |
| Transmittance | D1003 | 89% | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 20 g/10 min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| Bending temperature | 0.455MPa(66 psi) | D648 | 73℃(164℉) |
| 1.82MPa(264 psi) | D648 | 65℃(149℉) | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ASTM D648 | 135 °C |
| 1.8 MPa, 未退火，HDT | ASTM D648 | 125 °C |
| injection | Test Condition | Test Method | EASTMAN USA/6002 |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 280 to 290 °C | ||
| Temperature at the rear of the barrel | 265 to 275 °C | ||
| Processing (melt) temperature | 280 to 290 °C | ||
| drying temperature | 120 °C | ||
| Temperature | 60 to 80 °C | ||
| Spray nozzle temperature | 285 to 295 °C |