PA6

PA6 Ultramid® HPN9233G BK5830 BASF KOREA

229

Unit Price:US$ 3,272 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
41.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Oil resistant｜High impact resistance
Application Areas:Electrical enclosure｜film
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C	Internal Method	4.61 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	6.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break,23°C	ISO 527-2	175 Mpa
elongation	Break,23°C	ASTM D638	3.0 %
Tensile strain	Break,23°C	ISO 527-2	3.0 %
Bending modulus	23°C	ASTM D790	9380 Mpa
Bending modulus	Bending modulus	23°C	ISO 178	8400 Mpa
bending strength	23°C	ASTM D790	265 Mpa
tensile strength	Break,23°C	ASTM D638	175 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	174 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	208 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	54.0 °C
Melting temperature		ASTM D3418	220 °C
Melting temperature	Melting temperature		ISO 3146	220 °C
Linear coefficient of thermal expansion	MD	ASTME831	3.8E-05 cm/cm/°C
RTI Elec	0.71mm	UL 746	130 °C
	RTI Elec	1.5mm	UL 746	140 °C
		RTI Elec	3.0mm	UL 746	140 °C
		RTI Elec	RTI Elec	6.0mm	UL 746	140 °C
RTI Imp	0.71mm	UL 746	115 °C
	RTI Imp	1.5mm	UL 746	115 °C
		RTI Imp	3.0mm	UL 746	120 °C
		RTI Imp	RTI Imp	6.0mm	UL 746	120 °C
RTI Str	0.71mm	UL 746	140 °C
	RTI Str	1.5mm	UL 746	140 °C
		RTI Str	3.0mm	UL 746	140 °C
		RTI Str	RTI Str	6.0mm	UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.18mm		0.30 %
Water absorption rate	24hr	ASTM D570	1.1 %
	Water absorption rate	23°C,24hr	ISO 62	1.1 %
		Water absorption rate	Saturation	ASTM D570	6.4 %
			Water absorption rate	Saturation,23°C	ISO 62	6.4 %
				Water absorption rate	Equilibrium,50%RH	ASTM D570	1.8 %
				Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.8 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	>1.0E+13 ohms·cm
Dielectric strength	1.50mm	ASTM D149	22 KV/mm
Volume resistivity	1.50mm	ASTM D257	>1.0E+13 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.