Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 HPN9233G BK5830 BASF KOREA
Ultramid®
Electrical enclosure、film
Oil resistant、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF KOREA/HPN9233G BK5830 |
|---|---|---|---|
| Dart impact | 23°C | 内部方法 | 4.61 J |
| hardness | Test Condition | Test Method | BASF KOREA/HPN9233G BK5830 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | BASF KOREA/HPN9233G BK5830 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| Flexural modulus | 23°C | ISO 178 | 8400 Mpa |
| bending strength | 23°C | ASTM D790 | 265 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 175 Mpa |
| 断裂,23°C | ASTM D638 | 175 Mpa | |
| Flexural modulus | 23°C | ASTM D790 | 9380 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 3.0 % |
| Electrical performance | Test Condition | Test Method | BASF KOREA/HPN9233G BK5830 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| 1.50mm | ASTM D257 | >1.0E+13 ohms·cm | |
| dielectric strength | 1.50mm | ASTM D149 | 22 KV/mm |
| flammability | Test Condition | Test Method | BASF KOREA/HPN9233G BK5830 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 6.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF KOREA/HPN9233G BK5830 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.30 % | |
| Water absorption rate | 饱和 | ASTM D570 | 6.4 % |
| 24hr | ASTM D570 | 1.1 % | |
| 23°C,24hr | ISO 62 | 1.1 % | |
| 平衡,50%RH | ASTM D570 | 1.8 % | |
| 平衡,23°C,50%RH | ISO 62 | 1.8 % | |
| 饱和,23°C | ISO 62 | 6.4 % |
| Thermal performance | Test Condition | Test Method | BASF KOREA/HPN9233G BK5830 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 208 °C |
| RTI Elec | 6.0mm | UL 746 | 140 °C |
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| RTI Str | 6.0mm | UL 746 | 140 °C |
| melting temperature | ASTM D3418 | 220 °C | |
| RTI Elec | 0.71mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 140 °C | |
| RTI Imp | 3.0mm | UL 746 | 120 °C |
| melting temperature | ISO 3146 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 174 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 54.0 °C | |
| RTI Str | 1.5mm | UL 746 | 140 °C |
| 3.0mm | UL 746 | 140 °C | |
| RTI Elec | 1.5mm | UL 746 | 140 °C |
| Linear coefficient of thermal expansion | MD | ASTME831 | 3.8E-05 cm/cm/°C |
| RTI Imp | 0.71mm | UL 746 | 115 °C |
| 6.0mm | UL 746 | 120 °C | |
| RTI Str | 0.71mm | UL 746 | 140 °C |