PA66

PA66 Leona™ 14G15 ASAHI JAPAN

376

Unit Price:US$ 3,730 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
47.4MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Creep resistance｜Moderate heat resistance｜Thermal stability｜Fatigue resistance｜high strength｜High rigidity
Application Areas:Automotive sector｜Engine hood parts｜component｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
purpose			自动车部件
characteristic			高钢性.耐热

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	湿		2.1 %

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790/ISO 178	167 kg·cm/cm(J/M)ft·lb/in
Bending modulus		ASTM D790/ISO 178	4900 kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	M94
Charpy Notched Impact Strength		ASTM D256/ISO 179	49 kg·cm/cm(J/M)ft·lb/in
bending strength	干(湿)	ASTM D-790	167(108) Mpa
Elongation at Break	干(湿)	ASTM D-638	2.5(8) %
flexural coefficient	干(湿)	ASTM D-790	4.9(2.5) GPa
Rockwell hardness	干(湿)	ASTM D-785	120(-) R scale
Rockwell hardness	Rockwell hardness	干(湿)	ASTM D-785	94(71) M Scale
tensile strength	干(湿)	ASTM D-638	108(79) Mpa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	49(59) J/m

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	4 mm/mm.℃
Hot deformation temperature	HDT	ASTM D648/ISO 75	240 ℃（℉）
Combustibility (rate)		UL 94	HB
Hot deformation temperature	0.46MPa,干	ASTM D-648	258 °C
Hot deformation temperature	Hot deformation temperature	1.82MPa,干	ASTM D-648	240 °C
Linear coefficient of thermal expansion	干	ASTM D-696	4 ×10-5/K
UL flame retardant rating	干	UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate		ASTM D570/ISO 62	2.1 %
density		ASTM D792/ISO 1183	1.25
Wear factor	湿	ASTM D-1044	9 ×10-6kg/1000times
Shrinkage rate	干	旭化成方法	0.7/1.2 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.