Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 14G15 ASAHI JAPAN
Leona™
Automotive sector,Engine hood parts,component,Electronic field,Electrical field
Creep resistance,Moderate heat resistance,Thermal stability,Fatigue resistance,high strength,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/14G15 |
|---|---|---|---|
| Water absorption rate | 湿 | 2.1 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/14G15 |
|---|---|---|---|
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(-) R scale |
| 干(湿) | ASTM D-785 | 94(71) M Scale | |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 49(59) J/m |
| bending strength | 干(湿) | ASTM D-790 | 167(108) Mpa |
| flexural coefficient | 干(湿) | ASTM D-790 | 4.9(2.5) GPa |
| tensile strength | 干(湿) | ASTM D-638 | 108(79) Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 49 kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | ASTM D790/ISO 178 | 4900 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 167 kg·cm/cm(J/M)ft·lb/in | |
| Rockwell hardness | ASTM D785 | M94 | |
| elongation at break | 干(湿) | ASTM D-638 | 2.5(8) % |
| other | Test Condition | Test Method | ASAHI JAPAN/14G15 |
|---|---|---|---|
| characteristic | 高钢性.耐热 | ||
| purpose | 自动车部件 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/14G15 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 | |
| Water absorption rate | ASTM D570/ISO 62 | 2.1 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/14G15 |
|---|---|---|---|
| Wear factor | 湿 | ASTM D-1044 | 9 ×10-6kg/1000times |
| Shrinkage rate | 干 | 旭化成方法 | 0.7/1.2 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/14G15 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 1.82MPa,干，HDT | ASTM D-648 | 240 °C |
| HDT | ASTM D648/ISO 75 | 240 ℃（℉） | |
| 0.46MPa,干，HDT | ASTM D-648 | 258 °C | |
| UL flame retardant rating | 干 | UL 94 | HB |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 4 ×10-5/K |
| ASTM D696/ISO 11359 | 4 mm/mm.℃ |