POM TENAC™-C Z3510 ASAHIKASEI SUZHOU
222
- Unit Price:US$ 3,528 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:22MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact resistance｜Medium viscosity
- Application Areas:Electrical applications｜Household daily necessities｜Shell｜Application in the automotive field｜Engine parts｜Engineering accessories
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 78 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTM D648 | 158 °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 156 °C | |
| 1.8MPa,Unannealed | ASTM D648 | 110 °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 95.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |
| specific heat | 1470 J/kg/°C | ||
| thermal conductivity | 0.23 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm |
| Dielectric strength | ASTM D149 | 19 KV/mm | |
| Dielectric constant | 23°C,1MHz | ASTM D150 | 3.90 |
| Dissipation factor | 23°C,1MHz | ASTM D150 | 8E-03 |
| Arc resistance | ASTM D495 | 250 sec | |
| Surface resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.8 g/10min |
| Shrinkage rate | MD | Internal Method | 1.6-2.0 % |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| tensile strength | Yield | ISO 527-2 | 62.0 Mpa |
| -- | ASTM D638 | 62.0 Mpa | |
| elongation | Break | ASTMD638 | 40 % |
| Bending modulus | -- | ASTM D790 | 2450 Mpa |
| -- | ISO 178 | 2400 Mpa | |
| bending strength | ASTM D790 | 88.0 Mpa | |
| Taber abraser | ASTM D1044 | 14.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.