PPS LNP™ LUBRICOMP™ OCL-4536 BK SABIC INNOVATIVE US

301

Unit Price:US$ 6,160 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
42MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Flame retardant｜Filler: Carbon fiber reinforced material｜30%｜Filler by weight
Application Areas:Automotive components｜Electronic and electrical accessories
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	6.30	J
Multi axis Instrumented Impact Energy		ISO 6603-2	1.50	J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.2	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	14	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	230	Mpa
Bending modulus		ISO 178	19000	Mpa
Bending modulus	Bending modulus		ASTM D790	20100	Mpa
Tensile strain	Break	ISO 527-2	0.78	%
elongation	Break	ASTM D638	1.6	%
Tensile strain	Yield	ISO 527-2	0.77	%
elongation	Yield	ASTM D638	0.90	%
tensile strength	Break	ISO 527-2	113	Mpa
	tensile strength	Break	ASTM D638	119	Mpa
		tensile strength	Yield	ISO 527-2	113	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	128	Mpa
Tensile modulus		ISO 527-2/1	19900	Mpa
Tensile modulus	Tensile modulus		ASTM D638	18600	Mpa
bending strength		ISO 178	176	Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.36
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.30
Wear factor	Washer	ASTM D3702Modified	15.0	10^-10in^5-min/ft-lb-hr
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7E-06	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.2E-06	cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3.6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	3.6E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	248	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	259	°C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	272	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	274	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD:24hr	ISO 294-4	0.15	%
	Shrinkage rate	TD:24hr	ISO 294-4	0.66	%
		Shrinkage rate	TD：24hr	ASTM D955	0.70	%
		Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.20	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPS LNP™ LUBRICOMP™ OCL-4536 BK SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index