PPS OCL-4536 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components,Electronic and electrical accessories
Thermal stability,Flame retardant,Filler: Carbon fiber rein,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4536 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 14 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 1.50 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 3.2 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 6.30 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4536 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 19900 Mpa | |
| elongation | 屈服 | ASTM D638 | 0.90 % |
| bending strength | ASTM D790 | 230 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 0.77 % |
| tensile strength | 断裂 | ASTM D638 | 119 Mpa |
| 断裂 | ISO 527-2 | 113 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 15.0 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ASTM D790 | 20100 Mpa | |
| Tensile modulus | ASTM D638 | 18600 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.6 % |
| bending strength | ISO 178 | 176 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.30 |
| Tensile strain | 断裂 | ISO 527-2 | 0.78 % |
| Flexural modulus | ISO 178 | 19000 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 128 Mpa |
| 屈服 | ISO 527-2 | 113 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.36 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4536 BK |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.15 % |
| MD：24小时 | ASTM D955 | 0.20 % | |
| TD：24hr | ASTM D955 | 0.70 % | |
| TD:24小时 | ISO 294-4 | 0.66 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4536 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 272 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.2E-06 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 7E-06 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 274 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.6E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 3.6E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 248 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 259 °C |