Material Description

Material Properties:Easy to form｜Short molding cycle｜Low temperature and high ductility
Application Areas:Electrical appliances｜Architectural Applications｜Plastic bag｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	72.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	2.0 mm	UL 94	5VB
		UL flame retardant rating	3.0 mm	UL 94	5VA
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	800 °C
	Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	800 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2500 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350 Mpa
tensile strength	Yield3	ASTM D638	62.0 Mpa
	tensile strength	Yield	ISO 527-2/50	62.0 Mpa
		tensile strength	Break3	ASTM D638	54.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	58.0 Mpa
elongation	Yield3	ASTM D638	5.0 %
	elongation	Yield	ISO 527-2/50	5.0 %
		elongation	Break3	ASTM D638	100 %
		elongation	elongation	Break	ISO 527-2/50	100 %
Bending modulus	50.0 mm Span4	ASTM D790	2600 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2350 Mpa
bending strength	--5,6	ISO 178	90.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	95.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			90 to 100 °C
drying time			2.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			230 to 260 °C
Temperature in the middle of the barrel			250 to 290 °C
Temperature at the front of the material cylinder			260 to 300 °C
Spray nozzle temperature			250 to 290 °C
Processing (melt) temperature			270 to 300 °C
Mold temperature			60 to 90 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	128 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Be	125 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	114 °C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	119 °C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Ae	115 °C
Vicat softening temperature	--	ASTM D15259	134 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	135 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	7.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	5.9E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.0E-5 cm/cm/°C
RTI Elec		UL 746	100 °C
RTI Imp		UL 746	100 °C
RTI		UL 746	100 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	7.0 g/10 min
Melt Volume Flow Rate (MVR)	260°C/5.0 kg	ISO 1133	18.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.80 %
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength	3.20 mm, in Oil	ASTM D149	27 KV/mm
Compared to the anti leakage trace index		UL 746	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 2
High arc combustion index		UL 746	PLC 1
Hot wire ignition		UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.