Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML6411-76701 SABIC INNOVATIVE US
LEXAN™ 
Electrical appliances、Architectural Application、Plastic bag、Lighting applications
Easy to form、Short molding cycle、Low temperature and high
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/ML6411-76701
Dart impact23°C, Total EnergyASTM D376372.0 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/ML6411-76701
Tensile modulus--2ASTM D6382500 Mpa
tensile strength 屈服3ASTM D63862.0 Mpa
elongation断裂3ASTM D638100 %
断裂ISO 527-2/50100 %
Flexural modulus--5ISO 1782350 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79095.0 Mpa
--5,6ISO 17890.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902600 Mpa
tensile strength 断裂ISO 527-2/5058.0 Mpa
屈服ISO 527-2/5062.0 Mpa
elongation屈服ISO 527-2/505.0 %
屈服3ASTM D6385.0 %
tensile strength 断裂3ASTM D63854.0 Mpa
Tensile modulus--ISO 527-2/12350 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/ML6411-76701
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
dielectric strength3.20 mm, in OilASTM D14927 KV/mm
Volume resistivityIEC 60093> 1.0E+15 ohms·cm
Hot wire ignition (HWI)UL 746PLC 3
Compared to the Leakage Tracking Index (CTI)UL 746PLC 2
High arc combustion index (HAI)UL 746PLC 1
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/ML6411-76701
UL flame retardant rating3.0 mmUL 945VA
Hot filament ignition temperature2.0 mmIEC 60695-2-13800 °C
3.0 mmIEC 60695-2-13800 °C
UL flame retardant rating2.0 mmUL 945VB
Hot filament ignition temperature1.0 mmIEC 60695-2-13800 °C
UL flame retardant rating1.5 mmUL 94V-0
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
physical property Test ConditionTest MethodSABIC INNOVATIVE US/ML6411-76701
Water absorption rate平衡, 23°C, 50% RHISO 620.10 %
Melt volume flow rate260°C/5.0 kgISO 113318.0 cm3/10min
melt mass-flow rate260°C/2.16 kgASTM D12387.0 g/10 min
Water absorption rate饱和, 23°CISO 620.30 %
Shrinkage rate3.20 mm，Flow内部方法0.40 - 0.80 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/ML6411-76701
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8317.7E-5 cm/cm/°C
vicat--ASTM D15259134 °C
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距8，HDTISO 75-2/Be125 °C
Linear coefficient of thermal expansion横向 : -40°CISO 11359-27.0E-5 cm/cm/°C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
RTIUL 746100 °C
Heat distortion temperature0.45 MPa, 未退火, 6.40 mm，HDTASTM D648128 °C
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距8，HDTISO 75-2/Ae115 °C
vicat--ISO 306/B120135 °C
Linear coefficient of thermal expansion流动 : -40 到 40°CISO 11359-27.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 6.40 mm，HDTASTM D648119 °C
RTI ImpUL 746100 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8315.9E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648114 °C
RTI ElecUL 746100 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE US/ML6411-76701
drying time2.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Temperature in the middle of the barrel250 to 290 °C
Temperature at the rear of the barrel230 to 260 °C
Processing (melt) temperature270 to 300 °C
Hopper temperature60 to 80 °C
drying temperature90 to 100 °C
Temperature at the front of the material cylinder260 to 300 °C
Temperature60 to 90 °C
Spray nozzle temperature250 to 290 °C