PA66 Grilon® TSV0 EMS-CHEMIE SWITZERLAND
189
- Unit Price:US$ 4,654 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:53MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Thermal stability
- Application Areas:Automotive Applications｜Profile
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 干燥｜0.80 % | |
| ISO 294-4 | 干燥｜0.70 % | ||
| Water absorption rate | ISO 62 | 干燥｜8.0 % | |
| ISO 62 | 干燥｜2.5 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | UL 94 | 干燥｜V-0 | |
| UL 94 | 干燥｜V-0 | ||
| Limiting Oxygen Index | ISO 4589-2 | 干燥｜35 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 干燥｜3.0 kJ/m² | |
| ISO 179/1eA | 调节后｜3.0 kJ/m² | ||
| ISO 179/1eA | 干燥｜4.0 kJ/m² | ||
| ISO 179/1eA | 调节后｜15 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 干燥｜70 kJ/m² | |
| ISO 179/1eU | 调节后｜- kJ/m² | ||
| ISO 179/1eU | 干燥｜75 kJ/m² | ||
| ISO 179/1eU | 调节后｜100 kJ/m² | ||
| Tensile modulus | ISO 527-2 | 干燥｜3600 Mpa | |
| ISO 527-2 | 调节后｜1600 Mpa | ||
| tensile strength | 干燥｜85 Mpa | ||
| 调节后｜50 Mpa | |||
| ISO 527-2 | 干燥｜75 Mpa | ||
| ISO 527-2 | 调节后｜50 Mpa | ||
| Tensile strain | ISO 527-2 | 干燥｜4.0 % | |
| ISO 527-2 | 调节后｜15 % | ||
| Nominal tensile fracture strain | ISO 527-2 | 干燥｜10 % | |
| ISO 527-2 | 调节后｜＞50 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 调节后｜1.0E+10 ohms | |
| Volume resistivity | IEC 60093 | 干燥｜1.0E+13 ohms·cm | |
| IEC 60093 | 调节后｜1.0E+11 ohms·cm | ||
| dielectric strength | IEC 60243-1 | 干燥｜28 KV/mm | |
| IEC 60243-1 | 调节后｜26 KV/mm | ||
| relative permittivity | 干燥｜3.00 | ||
| 调节后｜8.00 | |||
| 干燥｜3.00 | |||
| 调节后｜4.00 | |||
| Dissipation Factor | 干燥｜5.0E-3 | ||
| 调节后｜0.15 | |||
| 干燥｜0.015 | |||
| 调节后｜0.070 | |||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Continuous use temperature | ISO 2578 | 干燥｜100 -120 °C | |
| 内部方法 | 干燥｜200 °C | ||
| melting temperature | ISO 11357-3 | 干燥｜260 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 干燥｜7.0E-5 cm/cm/°C | |
| ISO 11359-2 | 干燥｜9.0E-5 cm/cm/°C | ||
| Heat distortion temperature | ISO 75-2/A | 干燥｜210 °C | |
| ISO 75-2/C | 干燥｜70 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.