PA66 TSV0 EMS-CHEMIE SWITZERLAND
Grilon® 
Automotive Applications,Profile
Glass fiber reinforced,Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Other performanceTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSV0
Extreme Oxygen IndexISO 4589-2干燥｜35
Flammability levelUL 94干燥｜V-0
thermal performanceTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSV0
Continuous use temperature--3ISO 2578干燥｜100 -120 °C
--4Internal Method干燥｜200 °C
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/C干燥｜70 °C
0.45 MPa, UnannealedISO 75-2/A干燥｜210 °C
Linear coefficient of thermal expansionTDISO 11359-2干燥｜9.0E-5 cm/cm/°C
MDISO 11359-2干燥｜7.0E-5 cm/cm/°C
Melting temperatureISO 11357-3干燥｜260 °C
mechanical propertiesTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSV0
Charpy Notched Impact Strength-30°CISO 179/1eA调节后｜3.0 kJ/m²
23°CISO 179/1eA调节后｜15 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU调节后｜- kJ/m²
23°CISO 179/1eU调节后｜100 kJ/m²
Nominal tensile fracture strainISO 527-2调节后｜＞50 %
Tensile modulusISO 527-2调节后｜1600 Mpa
Tensile strainBreakISO 527-2调节后｜15 %
tensile strengthYield调节后｜50 Mpa
BreakISO 527-2调节后｜50 Mpa
Electrical performanceTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSV0
Compared to the anti leakage trace indexIEC 60112 V
Dielectric strengthIEC 60243-1调节后｜26 KV/mm
Dissipation factor1 MHz调节后｜0.070
100 Hz调节后｜0.15
Relative permittivity1 MHz调节后｜4.00
100 Hz调节后｜8.00
Surface resistivityIEC 60093调节后｜1.0E+10 ohms
Volume resistivityIEC 60093调节后｜1.0E+11 ohms·cm
Physical propertiesTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSV0
Shrinkage rateMDISO 294-4干燥｜0.70 %
TDISO 294-4干燥｜0.80 %
Water absorption rateSaturation, 23°CISO 62干燥｜8.0 %
Equilibrium, 23°C, 50% RHISO 62干燥｜2.5 %