LCP LAPEROS® C130 JAPAN POLYPLASTIC
205
- Unit Price:US$ 6,268 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High temperature resistance｜Glass fiber reinforced｜High mobility
- Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 80 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 250 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 255 °C | |
| 8.0 MPa, 未退火 | ISO 75-2/C | 211 °C | |
| vicat | ISO 306/B50 | 192 °C | |
| melting temperature | ISO 11357-3 | 325 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 6.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.8E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 45 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 28 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 20 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 26 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.62 g/cm³ | |
| shrinkage rate | 横向流量 | ISO 294-4 | 0.40 % |
| 流量 | ISO 294-4 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| relative permittivity | 100 Hz | IEC 60250 | 4.20 |
| 1 MHz | IEC 60250 | 3.70 | |
| Dissipation Factor | 100 Hz | IEC 60250 | 0.014 |
| 1 MHz | IEC 60250 | 0.018 | |
| arc resistance | 内部方法 | 182 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 150 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Hopper temperature | 20 to 30 °C | ||
| Temperature at the rear of the barrel | 290 to 300 °C | ||
| Temperature in the middle of the barrel | 300 to 310 °C | ||
| Temperature at the front of the material cylinder | 310 to 320 °C | ||
| Spray nozzle temperature | 310 to 330 °C | ||
| Processing (melt) temperature | 320 to 340 °C | ||
| mold temperature | 80 to 120 °C | ||
| injection speed | 快速 | ||
| Back pressure | < 3.00 Mpa |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 15000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 160 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.9 % |
| Tensile creep modulus | 1 hr | ISO 899-1 | 13600 Mpa |
| 1000 hr | ISO 899-1 | 11700 Mpa | |
| flexural modulus | 23°C | ISO 178 | 14000 Mpa |
| bending strength | 23°C | ISO 178 | 245 Mpa |
| Compression Modulus | ISO 604 | 22000 Mpa | |
| compression stress | 1% 应变 | ISO 604 | 139 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.