Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP C130 JAPAN POLYPLASTIC
LAPEROS®
Electrical field、Electronic field、Household appliances、Household appliances
Flame retardant、High temperature resistan、Glass fiber reinforced、High mobility
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 26 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 28 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 20 kJ/m² |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 80 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | 11700 Mpa |
| bending strength | 23°C | ISO 178 | 245 Mpa |
| Compression Modulus | ISO 604 | 22000 Mpa | |
| compression stress | 1% 应变 | ISO 604 | 139 Mpa |
| Flexural modulus | 23°C | ISO 178 | 14000 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 160 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.9 % |
| Tensile modulus | ISO 527-2/1A | 15000 Mpa | |
| Tensile creep modulus | 1 hr | ISO 899-1 | 13600 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 4.20 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.018 |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| arc resistance | 内部方法 | 182 sec | |
| Dissipation Factor | 100 Hz | IEC 60250 | 0.014 |
| relative permittivity | 1 MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 45 % |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| density | ISO 1183 | 1.62 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.20 % |
| 横向流量 | ISO 294-4 | 0.40 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 325 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 250 °C |
| vicat | ISO 306/B50 | 192 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 255 °C |
| 8.0 MPa, 未退火，HDT | ISO 75-2/C | 211 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 6.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.8E-5 cm/cm/°C |
| injection | Test Condition | Test Method | JAPAN POLYPLASTIC/C130 |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature in the middle of the barrel | 300 to 310 °C | ||
| Temperature at the rear of the barrel | 290 to 300 °C | ||
| Processing (melt) temperature | 320 to 340 °C | ||
| Hopper temperature | 20 to 30 °C | ||
| drying temperature | 150 °C | ||
| Temperature at the front of the material cylinder | 310 to 320 °C | ||
| Back pressure | < 3.00 Mpa | ||
| Temperature | 80 to 120 °C | ||
| injection speed | 快速 | ||
| Spray nozzle temperature | 310 to 330 °C |