PA12 Pebax® 5533 SP 01 ARKEMA FRANCE

397
  • Unit Price:US$ 22,273 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High temperature resistance｜Low temperature resistance
  • Application Areas:Medical Supplies
  • Color:--
  • Grade:Flame retardant enhanced grade

Technical Data Sheet

Filling analysisTest ConditionTest MethodTest Result
Melt density0.830 g/cm³
Thermal conductivity of melt0.18 W/m/K
Specific Heat Capacity of Melt2800 J/kg/°C
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
flammabilityTest ConditionTest MethodTest Result
Flammability levelUL 94HB
elastomerTest ConditionTest MethodTest Result
tear strengthISO 34-1110 kN/m
Permanent compression deformation23°CISO 81543 %
squeeze outTest ConditionTest MethodTest Result
drying temperature65 to 75 °C
drying time4.0 to 6.0 hr
Melt Temperature210 to 230 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-2170 Mpa
tensile strengthYieldISO 527-212.0 Mpa
Wear resistanceISO 464947.0 mm³
Nominal tensile fracture strainISO 527-2> 50 %
Tensile strainBreakISO 527-2> 300 %
Tensile strainYieldISO 527-225 %
tensile strength100% StrainISO 527-214.0 Mpa
tensile strength10% StrainISO 527-210.0 Mpa
tensile strengthBreakISO 527-252.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature65 to 75 °C
drying time4.0 to 6.0 hr
Processing (melt) temperature200 to 270 °C
Mold temperature25 to 60 °C
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B66.0 °C
Vicat softening temperatureISO 306/B50142 °C
Melting temperatureISO 11357-3159 °C
Linear coefficient of thermal expansionFlowISO 11359-21.7E-4 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rate横向FlowISO 294-41.4 %
Shrinkage rateFlowISO 294-41.2 %
Water absorption rateSaturation, 23°CISO 621.2 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.60 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 60093-- ohms
Volume resistivityIEC 600933.2E+13 ohms·cm
Dielectric strengthIEC 60243-139 KV/mm
Relative permittivity100 HzIEC 602509.00
Relative permittivity1 MHzIEC 602505.00
Dissipation factor100 HzIEC 602500.11
Dissipation factor1 MHzIEC 602500.10
Compared to the anti leakage trace indexIEC 60112 V
hardnessTest ConditionTest MethodTest Result
Shore hardnessShore D, 15 SecISO 7619-150
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.