Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 5533 SP 01 ARKEMA FRANCE
Pebax®
Medical Supplies
High temperature resistan、Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| hardness | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| Shore hardness | 邵氏 D, 15 秒 | ISO 7619-1 | 50 |
| Mechanical properties | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 170 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | > 50 % | |
| Tensile strain | 断裂 | ISO 527-2 | > 300 % |
| 屈服 | ISO 527-2 | 25 % | |
| wear resistance | ISO 4649 | 47.0 mm³ | |
| tensile strength | 断裂 | ISO 527-2 | 52.0 Mpa |
| 屈服 | ISO 527-2 | 12.0 Mpa | |
| 10% 应变 | ISO 527-2 | 10.0 Mpa | |
| 100% 应变 | ISO 527-2 | 14.0 Mpa |
| Electrical performance | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 9.00 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.10 |
| dielectric strength | IEC 60243-1 | 39 KV/mm | |
| Volume resistivity | IEC 60093 | 3.2E+13 ohms·cm | |
| Dissipation Factor | 100 Hz | IEC 60250 | 0.11 |
| relative permittivity | 1 MHz | IEC 60250 | 5.00 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| Flammability level | UL 94 | HB |
| Filling analysis | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| Melt density | 0.830 g/cm³ | ||
| Specific Heat Capacity of Melt | 2800 J/kg/°C | ||
| Thermal conductivity of melt | 0.18 W/m/K |
| squeeze out | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| drying temperature | 65 to 75 °C | ||
| Melt Temperature | 210 to 230 °C | ||
| drying time | 4.0 to 6.0 hr |
| physical property | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.60 % |
| Shrinkage rate | 流量 | ISO 294-4 | 1.2 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 1.2 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.4 % |
| elastomer | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| compression set | 23°C | ISO 815 | 43 % |
| tear strength | ISO 34-1 | 110 kN/m |
| Thermal performance | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 159 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 66.0 °C |
| vicat | ISO 306/B50 | 142 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.7E-4 cm/cm/°C |
| injection | Test Condition | Test Method | ARKEMA FRANCE/5533 SP 01 |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| Processing (melt) temperature | 200 to 270 °C | ||
| drying temperature | 65 to 75 °C | ||
| Temperature | 25 to 60 °C |