ABS Toyolac® 920 TORAY JAPAN

670

Unit Price:US$ 2,620 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS TR557 LG CHEM KOREA

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High rigidity｜transparent
Application Areas:small home appliances｜Casters｜sporting goods｜Automotive sector｜Electrical field｜Electronic field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			透明性.超高刚性
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break	23℃	ASTM D-638	380	kg/cm
bending strength	23℃	ASTM D-790	780	kg/cm
Impact strength of cantilever beam gap	3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃	ASTM D-256	10；7；6	kg.cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃	ASTM D-256	9；7；6	kg.cm/cm
Bending stress	23℃	ASTM D-790	23500	kg/cm
Tensile strength at break	23℃	ASTM D-638	30	%
Tensile strength under yield	23℃	ASTM D-638	3.5	%
Rockwell hardness	23℃	ASTM D-785	115	R
tensile strength	23℃，Yield	ASTM D-638	490	kg/cm
Impact strength of cantilever beam gap		ASTM D256/ISO 179	108	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	74	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2160	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	115
tensile strength		ASTM D638/ISO 527	48	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	20	%
Tensile stress	23℃	ISO 527-2	54.0	Mpa
Tensile strain	23℃，Break	ISO 527-2	17	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion		ASTM D-696	1.2×10	mm/mm/℃
Hot deformation temperature	HDT	ASTM D648/ISO 75	83	℃（℉）
Combustibility (rate)		UL 94	HB
Hot deformation temperature	18.56kg/cm	ASTM D-648	89	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa，Unannealed	ISO 75-2/A	77.0	°C
UL flame retardant rating		UL 94	HB
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	220℃		3.5-5.0
Combustibility		UL -94	94HB
melt mass-flow rate	220℃ 10kg	ASTM D-1238	19-23	g/10min
Water absorption rate	浸入23℃水中24hr	ASTM D-570	0.3	%
melt mass-flow rate		ASTM D1238/ISO 1133	25	g/10min
density		ASTM D792/ISO 1183	1.09
melt mass-flow rate	220℃/10kg	ISO 1133	25	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Weihang	US$ 2250 /MT

Supplier Join

Get App

Top

ABS Toyolac® 920 TORAY JAPAN

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index