Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 920 TORAY JAPAN
Toyolac®
small home appliances、Casters、sporting goods、Automotive sector、Electrical field、Electronic field
High mobility、High rigidity、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/920 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 74 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 108 kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | ASTM D790/ISO 178 | 2160 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | 23℃ | ASTM D-638 | 380 kg/cm |
| Tensile stress | 23℃ | ISO 527-2 | 54.0 Mpa |
| Tensile strength at break | 23℃ | ASTM D-638 | 30 % |
| elongation at break | ASTM D638/ISO 527 | 20 % | |
| Rockwell hardness | ASTM D785 | 115 | |
| tensile strength | ASTM D638/ISO 527 | 48 kg/cm²(MPa)[Lb/in²] | |
| Bending stress | 23℃ | ASTM D-790 | 23500 kg/cm |
| Impact strength of cantilever beam gap | 3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | ASTM D-256 | 10；7；6 kg.cm/cm |
| Tensile strain | 23℃，断裂 | ISO 527-2 | 17 % |
| bending strength | 23℃ | ASTM D-790 | 780 kg/cm |
| tensile strength | 23℃，屈服 | ASTM D-638 | 490 kg/cm |
| Impact strength of cantilever beam gap | 12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | ASTM D-256 | 9；7；6 kg.cm/cm |
| Tensile strength under yield | 23℃ | ASTM D-638 | 3.5 % |
| Rockwell hardness | 23℃ | ASTM D-785 | 115 R |
| other | Test Condition | Test Method | TORAY JAPAN/920 |
|---|---|---|---|
| characteristic | 透明性.超高刚性 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/920 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 25 g/10min |
| physical property | Test Condition | Test Method | TORAY JAPAN/920 |
|---|---|---|---|
| Water absorption rate | 浸入23℃水中24小时 | ASTM D-570 | 0.3 % |
| combustibility | UL -94 | 94HB | |
| melt mass-flow rate | 220℃ 10kg | ASTM D-1238 | 19-23 g/10min |
| melt viscosity | 220℃ | 3.5-5.0 | |
| melt mass-flow rate | 220℃/10kg | ISO 1133 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/920 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 18.56kg/cm，HDT | ASTM D-648 | 89 °C |
| HDT | ASTM D648/ISO 75 | 83 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D-696 | 1.2×10 mm/mm/℃ | |
| Heat distortion temperature | 1.8MPa，未退火，HDT | ISO 75-2/A | 77.0 °C |
| UL flame retardant rating | UL 94 | HB |