Material Description

Material Properties:Flame retardant｜enhance｜Glass fiber reinforced
Application Areas:Automotive Applications｜Home appliance components
Color:--
Grade:Injection grade

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result
density		ISO 1183	1620 kg/m

mechanical properties	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23℃	ISO 180/1U	33.0 KJ/m
Charpy Notched Impact Strength	23℃	ISO 179/1eA	26.0 KJ/m
bending strength	23℃	ISO 178	210 Mpa
Bending modulus	23℃	ISO 178	10500 Mpa
elongation	Break	ISO 527-1	3.3 %
tensile strength		ISO 527-1	175 Mpa
Tensile modulus		ISO 527-1	11000 Mpa
Rockwell hardness		ISO 2039-2	55 M Scale
Impact strength of cantilever beam gap	23℃	ISO 180/1A	23.0 KJ/m
Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	38.0 KJ/m

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	50℃/h 50N	ISO 306	146 °C
Hot deformation temperature	8.00MPa	ISO 75-1	162 °C
Hot deformation temperature	Hot deformation temperature	1.80MPa	ISO 75-1	230 °C
Crystallization peak temperature	10℃/min	ISO 11357-1	280 °C
Linear coefficient of thermal expansion	parallel	ISO 11359-1	0.0 cm/cm℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	normal	ISO 11359-1	0.000019 cm/cm℃
Combustibility		UL 94	V-0
Hot deformation temperature	0.45MPa	ISO 75-1	250 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	parallel	ISO 2577	0.40 %
Shrinkage rate	Shrinkage rate	normal	ISO 2577	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric loss	100Hz	IEC 60250	0.020
Relative permittivity	1000Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.50
Volume resistivity		IEC 60093	1E+13 ohm.m
Dielectric strength		IEC 60243-1	32 KV/mm
Compared to the Leakage Traceability Index (CTI)		IEC 60112	175
Dielectric loss	1000Hz	IEC 60250	0.016
Surface resistivity		IEC 60093	>1.0E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LCP VECTRA® A435 CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet