Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP A435 CELANESE USA
VECTRA®
Automotive Applications、Home appliance components
Flame retardant、enhance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | CELANESE USA/A435 |
|---|---|---|---|
| density | ISO 1183 | 1620 kg/m |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/A435 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | 38.0 KJ/m |
| Suspended wall beam without notch impact strength | 23℃ | ISO 180/1U | 33.0 KJ/m |
| Flexural modulus | 23℃ | ISO 178 | 10500 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 23.0 KJ/m |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 26.0 KJ/m |
| Tensile modulus | ISO 527-1 | 11000 Mpa | |
| Rockwell hardness | ISO 2039-2 | 55 M Scale | |
| tensile strength | ISO 527-1 | 175 Mpa | |
| elongation | 断裂 | ISO 527-1 | 3.3 % |
| bending strength | 23℃ | ISO 178 | 210 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/A435 |
|---|---|---|---|
| relative permittivity | 1000Hz | IEC 60250 | 3.10 |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| Volume resistivity | IEC 60093 | 1E+13 ohm.m | |
| Dielectric loss | 100Hz | IEC 60250 | 0.020 |
| Compared to the Leakage Traceability Index (CTI) | IEC 60112 | 175 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dielectric loss | 1000Hz | IEC 60250 | 0.016 |
| physical property | Test Condition | Test Method | CELANESE USA/A435 |
|---|---|---|---|
| Shrinkage rate | parallel | ISO 2577 | 0.40 % |
| normal | ISO 2577 | 0.10 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/A435 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-1 | 250 °C |
| Linear coefficient of thermal expansion | normal | ISO 11359-1 | 0.000019 cm/cm℃ |
| Crystallization peak temperature | 10℃/min | ISO 11357-1 | 280 °C |
| Linear coefficient of thermal expansion | parallel | ISO 11359-1 | 0.0 cm/cm℃ |
| combustibility | UL 94 | V-0 | |
| Heat distortion temperature | 1.80MPa，HDT | ISO 75-1 | 230 °C |
| vicat | 50℃/h 50N | ISO 306 | 146 °C |
| Heat distortion temperature | 8.00MPa，HDT | ISO 75-1 | 162 °C |